ULTEM™ 1285 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TISTzc_ULTEM1285resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (295°C/6.6 kg) | 8.1 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3380 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 110 | MPa | ASTM D638 |
| Fracture | 82.7 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3380 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 950 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 40.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 165 | °C | ASTM D648 |
| Vicat Softening Temperature | 181 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 282 - 316 | °C | |
| Middle Temperature | 288 - 321 | °C | |
| Front Temperature | 293 - 327 | °C | |
| Nozzle Temperature | 299 - 332 | °C | |
| Processing (Melt) Temp | 299 - 332 | °C | |
| Mold Temperature | 93.3 - 149 | °C | |
| Back Pressure | 0.689 - 1.38 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4PROP® 5C40800 | 4Plas | PP Copolymer | 4PROP® |
| Cellophane™ 500PUT | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| GLS PP ZT79 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| ESTADIENE CR 1 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Sylvin 9067-80 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |