TRANSMARE® 14CGF40-0.001
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TIDdlx_TRANSMARE-14CGF40-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 14CGF40-0.001 is a 40 % glass fiber reinforced polypropylene copolymer for injection molding purposes with high stiffness, high impact and a good flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 5.5 | g/10 min | |
| 230°C/5.0 kg | 18 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 90.0 | MPa | |
| Break, 4.00 mm | 90.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 4.0 | % | |
| Break, 4.00 mm | 5.0 | % | |
| Flexural Modulus 1 | 7700 | MPa | ISO 178 |
| Flexural Stress 2 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 12 | kJ/m² | |
| -20°C | 12 | kJ/m² | |
| 0°C | 13 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 13 | kJ/m² | |
| -20°C | 16 | kJ/m² | |
| 0°C | 16 | kJ/m² | |
| 23°C | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 139 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 159 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol H-622 | Shanghai Suptech Engineering Plastics Co. Ltd. | TPO (POE) | Supol |
| NYCOA Polyamide 6033 HS Black | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| AEI TP543C | AEI Compounds Limited | PE, Unspecified | AEI |
| Firestone CG430-203 | Firestone Textiles Company | Nylon 6 | Firestone |
| Five Plus™ CPP20C | Noble Polymers | PP Copolymer | Five Plus™ |