Laticonther 87/28 GR/50
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TIBG87_Laticonther-87-28-GR-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High thermal conductivity product based on Polycarbonate (PC). Graphite. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.75 | % | |
| Flow : 2.00 mm | 0.45 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.80 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Thermal Conductivity | 10 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P485 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Hostacom PPR 1042 101070 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Piolen® P G30CA63 | PiO Kunststoffe GmbH & Co KG | PP Copolymer | Piolen® P |
| Hostacom M2 R18 NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LUVOCOM® 1105-8099/GY | LEHVOSS Group | PEEK | LUVOCOM® |