Nymax™ GF 1200 A 33 HS Natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | THAIgR_Nymax-GF-1200-A-33-HS-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nymax of nylon 6/6 polymers reinforced with glass fibers®GF 1200 series products are specially used in harsh environments and have the characteristics of high rigidity, tensile properties, heat resistance, durability, etc. According to the needs of rigid characteristics, these materials have a large range of strength and are easy to process in standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 193 | MPa | ISO 527-2 |
| Fracture 1 | 197 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 9430 | MPa | ISO 899-1 |
| 1000 hr | 6310 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| -- | 68.4 | MPa | ISO 178 |
| -- | 8960 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- | 230 | MPa | ISO 178 |
| -- | 276 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 130 | J/m | ASTM D256A |
| -- | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 246 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.18mm | 250 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.9E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information |
|---|
| 模制试验条：模制时干燥 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 60.0 - 107 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 53 H 10-81 | Ravago Group | PP Homopolymer | Scolefin |
| SCHULABLEND® (ABS/PA) M/MK | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |
| EverGlide® MB2650 | Polymer Dynamix | SBC | EverGlide® |
| Plaslube® TPU T/AL27 | Techmer Engineered Solutions | TPU-Polyester | Plaslube® |
| PLUSTEK PA301G7 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |