DINALON® PA 6.6 15% FV
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Grupo Repol |
| Trademark: | DINALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TGcvr3_DINALON-PA-6-6-15-FV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINALON®PA 6.6 15% FV is a polyamide 66 (nylon 66) product containing 15% glass fiber reinforcement. It can be processed by injection molding and is available in Europe. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 4800 | MPa | ASTM D790 |
| Flexural Strength | 150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 200 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Glow Wire, UNE 20-672-83: 650°CVicat Softening Temperature, ASTM D1525: >200°CDTUL, ASTM D648: 190°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 275 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Daplen™ EG251AIB | Borealis AG | TPO | Daplen™ |
| HAIPLEN H30 K6 BA X0 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Karina BLUE PVC COMPOUND 804-02/39-Y-RTC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PERLER® O07N0000B00 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |
| LEXAN™ 9915A_ resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |