Ultramid® C3U BK23079
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TGbsMZ_Ultramid-C3U-BK23079.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid C3U BK23079 is an injection molding, general purpose PA6/66, pigmented black grade with improved flame retardance. The product is UL recognized as 94V0 at 0.4 mm minimum thickness. Applications It is used for impact resistant electrical insulating parts such as contact bases and plug connector strips. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 8.5 | % | |
| Equilibrium, 23°C, 50% RH | 2.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3770 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 84.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.7 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 69 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 68.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 243 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.380 mm | 110 | °C | |
| 0.750 mm | 120 | °C | |
| 1.50 mm | 120 | °C | |
| 3.00 mm | 120 | °C | |
| RTI Imp | UL 746 | ||
| 0.380 mm | 65.0 | °C | |
| 0.750 mm | 105 | °C | |
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| RTI Str | UL 746 | ||
| 0.380 mm | 65.0 | °C | |
| 0.750 mm | 115 | °C | |
| 1.50 mm | 120 | °C | |
| 3.00 mm | 120 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® 22LH-NBK4 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Ultramid® B3GM35 BKQ642 23220 | BASF Corporation | Nylon 6 | Ultramid® |
| Axiall PVC 8820 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| DynaMix™ 3201-L | Polymer Dynamix | PEEK | DynaMix™ |
| Karina BLACK PVC COMPOUND 450-48/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |