RheTech Polypropylene HP515-00
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TFuXZ0_RheTech-Polypropylene-HP515-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Talc Reinforced, High Performance, Non-UV Stabilized, Polypropylene Copolymer, Natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 38 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 26.2 | MPa | ASTM D638 |
| Flexural Modulus | 2030 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Dart Drop Impact | 13.6 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 126 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 63.3 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 193 - 221 | °C | |
| Middle Temperature | 199 - 227 | °C | |
| Front Temperature | 204 - 232 | °C | |
| Nozzle Temperature | 210 - 221 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable, Application DependentScrew RPM: Recovery 3 Seconds Before Mold OpensCycle Time: Wall Thickness Dependent |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 0292N-NE | TSRC Corporation | SEBS | T-Blend® |
| TRIBOCOMP® PA66 GF30 TS13 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| Bayblend® M750 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Compoceran P501 | Arakawa Chemical Industries, Ltd. | Phenolic | Compoceran |
| Generic Nylon 410 | Generic | Nylon 410 | Generic |