Crastin庐 SK601 NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TF7Lho_Crastin-SK601-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass Reinforced Polybutylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 18 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.40 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | |
| Viscosity Number | 110 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.7 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 4000 | MPa | |
| 1000 hr | 2500 | MPa | |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 26 | kJ/m² | |
| 23°C | 27 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 175 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 | ||
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 36 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 20 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.19 | g/cm³ | |
| Specific Heat Capacity of Melt | 1890 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.24 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EUROPLEX® Sheet GV 181 | Evonik Industries AG | PC | EUROPLEX® Sheet |
| EPO-TEK® 310T-M | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| HONES® PPS HS-G30 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| Latiohm 66-06 PD03 G/20 | LATI S.p.A. | Nylon 66 | Latiohm |
| ISORENE™ CA8-7001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |