Ultramid® A3HG6 HR
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TEaH4w_UltramidA3HG6HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3HG6 HR is a 30% glass reinforced, injection molding PA66 grade. It offers good resistance to hydrolysis. Applications Typical applications include automotive radiator mounting frame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | 25.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 5.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10100 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 188 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.3 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8850 | MPa | ISO 178 |
| Flexural Stress (23°C) | 275 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 9.0 | kJ/m² | ISO 179 |
| 23°C | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 63 | kJ/m² | ISO 179 |
| 23°C | 77 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180 | ||
| -40°C | 8.3 | kJ/m² | ISO 180 |
| 23°C | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 249 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 - 305 | °C | |
| Mold Temperature | 80 - 90 | °C | |
| Injection Pressure | 3.50 - 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PR023 | Premier Polymers, LLC. | PP Random Copolymer | Premier |
| Prime Polypro™ F337D | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| TOTAL Polystyrene Impact 940E | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| NEFTEKHIM PE 4223V (23416) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| DURACON® EB-08 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |