INELEC PSUCF15
| Category: | PSU , Polysulfone |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INELEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TEMygq_INELEC-PSUCF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% CARBON FIBER FILLED POLYSULFONE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 182 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 327 to 371 | °C | |
| Middle Temperature | 327 to 371 | °C | |
| Front Temperature | 327 to 371 | °C | |
| Processing (Melt) Temp | 338 to 349 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V931 BLK588 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Prime Polypro™ JR-3070HP | Prime Polymer Co., Ltd. | PP Impact Copolymer | Prime Polypro™ |
| Starpylen HU 30BF4 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Hostalen PP H1850 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| SHINSTRA WG30TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |