TRIBOCOMP® PA6 CF10 TS0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TDzDyQ_TRIBOCOMP-PA6-CF10-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PA6 CF10 TS0 is a polyamide 6 (nylon 6) product, which contains 20% ptfe fiber and 10% carbon fiber reinforced materials. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7200 | 4400 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 130 | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6100 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | -- | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | |||
| Dynamic | 0.13 | -- | ASTM D3702 | |
| Static | 0.12 | -- | ASTM D3702 | |
| Wear Factor | 11.0 | -- | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | 45 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 3.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.43 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+6 | -- | ohms | ASTM D257 |
| Additional Information |
|---|
| 干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 230 - 270 | °C | |
| Middle Temperature | 235 - 280 | °C | |
| Front Temperature | 235 - 280 | °C | |
| Nozzle Temperature | 235 - 290 | °C | |
| Processing (Melt) Temp | < 320 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tekulac ST 50 FR | TEKUMA Kunststoff GmbH | ABS | Tekulac |
| VESTAMID® NRG 1001 natural color | Evonik Industries AG | Nylon 12 | VESTAMID® NRG |
| Vandar® 4612R | Celanese Corporation | PBT | Vandar® |
| Flexirene® CM 50 | Versalis S.p.A. | LLDPE | Flexirene® |
| LNP™ THERMOCOMP™ DX06410 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |