Ultramid® B3S Q661
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TDoi3y_Ultramid-B3S-Q661.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3S Q661 is a general purpose, PA6 resin for injection molding. Applications Ultramid B3S Q661 is suitable for wide range of applications due to its rapid cycling and excellent physical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 145 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 79.0 | MPa | ASTM D638 |
| Yield, 23°C | 85.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 3.8 | % | ISO 527-2 |
| Break, 23°C | 4.2 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2740 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 180 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 76.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 110 | °C | |
| 3.00 mm | 115 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC C8070 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| APEX® 3300-70NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Daelim Po1y® PP-247H | DAELIM INDUSTRIAL CO., LTD. | PP Impact Copolymer | Daelim Po1y® |
| Epic Epoxy R1074-06/H4030-02 | Epic Resins | Epoxy | Epic Epoxy |
| Therma-Tech™ TT9200-5010 EC Anthracite | PolyOne Corporation | PPS | Therma-Tech™ |