Trexprene® A40NU
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TDmMqO_Trexprene-A40NU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A40NU is a heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This Natural compound is intended primarily for underhood applications such as mats, seals, gaskets, air ducts, CVJ boots, covers, grommets or other parts where softness and conformity are needed. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 to 0.940 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 38 to 44 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 1(100% Strain) | 1.10 | MPa | ISO 37 |
| Tensile Stress - Across Flow 2(Yield) | 3.00 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 3(Break) | 300 | % | ISO 37 |
| Tear Strength - Across Flow 4 | 12 | kN/m | ISO 34-1 |
| Compression Set | |||
| 70°C, 22 hr | 30 | % | ASTM D395B |
| 125°C, 70 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr 5 | 30 | % | ISO 815 |
| 125°C, 70 hr 6 | 20 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ISO 188 | ||
| 135°C, 1000 hr | -25 to 10 | % | |
| 150°C, 168 hr | -20 to 10 | % | |
| Change in Tensile Strain at Break in Air | ISO 188 | ||
| 135°C, 1000 hr | -30 to 10 | % | |
| 150°C, 168 hr | -25 to 10 | % | |
| Change in Shore Hardness in Air | ISO 188 | ||
| Shore A, 135°C, 1000 hr | -5.0 to 5.0 | ||
| Shore A, 150°C, 168 hr | -3.0 to 3.0 | ||
| Change in Tensile Properties | ISO 188 | ||
| Stress at 100% Elongation in Air, 1000 hrs : 135°C | -20 to 20 | % | |
| Stress at 100% Elongation in Air, 168 hrs : 150°C | -20 to 20 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance (40°C) 7 | 0 Rating | ISO 1431-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -56.0 | °C | ASTM D746 |
| Type B | -56.0 | °C | ISO 812 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | Type A |
| 7 . | 100 pphm, Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecolen® HP10 GR30 NL HS | Eurotec Engineering Plastics | PP Homopolymer | Tecolen® |
| Versaflex™ OM 1060X-9 | PolyOne Corporation | TPE | Versaflex™ |
| Delrin® 100 BK602 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Dryflex® XP 1501 | ELASTO | TPE | Dryflex® |
| Lupolen 3220 F | LyondellBasell Industries | LDPE | Lupolen |