UBE Nylon 5034 B Datasheet,Nylon 66/6,UBE Engineering Plastics, S.A.-SHANGHAI SUSHENG

Message
Ube Nylon 5034B is a PA6/6.6 Copolyamide, produced by continuous polymerization process. It is a high viscosity grade suitable for numerous applications. The grade can be used for cast film and blown film (air cooled).

General Information
Additive	Low smoothness
Features	Low smoothness Workability, good Compliance of Food Exposure Viscosity, High
Uses	Films cast film
Agency Ratings	European food contact, not rated
Appearance	Natural color
Forms	Particle
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	1.0	ASTM D1894
With Self-Static	1.0	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD	400	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield	23.0	MPa	ASTM D882
Fracture	107	MPa	ASTM D882
Tensile Elongation - MD (Break)	600	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	192	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	155		ASTM D523
Haze	0.50	%	ASTM D1003

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 41.5 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.08Surface Resistivity, UBE Method: >1e15 ohmExtractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 80/20Water Vapor Permeability, JIS Z0208: 130 g/m²/dayPiercing Strength, JAS P1019: 950 N/mmPiercing Elongation, JAS P1019: 14.5 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle: <5 hole/0.04 m²

Additional Information

The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 41.5 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.08Surface Resistivity, UBE Method: >1e15 ohmExtractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 80/20Water Vapor Permeability, JIS Z0208: 130 g/m²/dayPiercing Strength, JAS P1019: 950 N/mmPiercing Elongation, JAS P1019: 14.5 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle: <5 hole/0.04 m²

Resin Grade	Manufacturer	Category	Trademark
Sylvin 8984-95 Black	Sylvin Technologies Incorporated	PVC, Flexible	Sylvin
ExxonMobil™ PP1063L1	ExxonMobil Chemical	PP Homopolymer	ExxonMobil™
Generic PPA - Mineral	Generic	PPA	Generic
Generic Nylon 6+PP - Glass Fiber	Generic	Nylon 6+PP	Generic
Hanwha Total PP HJ700	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP Homopolymer	Hanwha Total PP

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TDgAsg_UBE-Nylon-5034-B.pdf
PRICE:	Order Products email sales@su-jiao.com