Cevian®-V 110
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TDCpd0_Cevian--V-110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cevian®-V 110 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 46.9 | MPa | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.18 mm | 200 | J/m | ASTM D256 |
| 6.35 mm | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 92.8 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Specific Gravity, ASTM D792, 73°F, 50% RH: 1.05Melt Flow Rate, ASTM D1238, 230°C, 5 kg: 9 g/10 minWater Absorption, ASTM D570, 73°F, 24 hr: 0.3 %Deflection Temperature Under Load, ASTM D648, 264 psi, unannealed, 0.250": 190°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 188 - 199 | °C | |
| Middle Temperature | 210 - 221 | °C | |
| Front Temperature | 221 - 232 | °C | |
| Processing (Melt) Temp | 232 - 243 | °C | |
| Mold Temperature | 48.9 - 60.0 | °C | |
| Injection Pressure | 34.5 - 103 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.689 - 2.07 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitalac® 1002 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| Nylene® 6110 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Arnite® AV2 390 | DSM Engineering Plastics | PET | Arnite® |
| Emulprene® 1006 | INSA | SBR, Emulsion | Emulprene® |
| Hylon® N2040MG10HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |