AKROMID® A3 black (3706)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TCa7GG_AKROMID-A3-black-3706-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 black (3706) is an unreinforced, heat stabilised polyamide 6.6. Applications are components with thin walls and long flow paths |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 104 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.6 | -- | % | |
| Flow | 1.4 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.9 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 7.0 | 9.0 | % | ISO 178 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 144 | 87.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 80.0 | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | > 5.0 | -- | % | |
| Break | > 15 | > 50 | % | |
| Flexural Modulus 2 | 2800 | 1400 | MPa | ISO 178 |
| Flexural Stress 3 | 110 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.5 | -- | kJ/m² | |
| 23°C | 7.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 7.0 | -- | kJ/m² | |
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 8.0 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 209 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 47.0 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 260 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 400 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Fiberfil® J-60/20/E/NS | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Huafon JF-A-AH5022 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| ICORENE® N2105 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |
| TPX® MX004XB | Mitsui Chemicals, Inc. | PMP Copolymer | TPX® |