Desmopan® 9385 A
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TCXeq8_Desmopan-9385-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; very good hydrolysis and microbial resistance; good low-temperature flexibility; complies with VDE 0282-10; Application; Cable sheathings; Hoses, non-reinforced |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 23°C | 86 | ||
| Shore D, 23°C | 35 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| 10% Strain, 23°C | 2.00 | MPa | |
| 50% Strain, 23°C | 5.30 | MPa | |
| Abrasion Resistance (23°C) | 25.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 18.0 | MPa | |
| 20°C | 32.0 | MPa | |
| 60°C | 23.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 40 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2 | DIN 53504 | ||
| 100% Strain, 23°C | 6.80 | MPa | |
| 300% Strain, 23°C | 12.2 | MPa | |
| Tensile Stress 3(Break, 23°C) | 39.1 | MPa | DIN 53504 |
| Tensile Elongation 4(Break, 23°C) | 600 | % | DIN 53504 |
| Tear Strength 5(23°C) | 65 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | |
| 70°C, 24 hr | 43 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Processing (Melt) Temp | 205 to 225 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Melt Temperature | 195 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP PHC27-90 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Mowiol® 30-98 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| TAROMID A 280 Z1 G6 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Ferro PP TPP25AP94NA | Ferro Corporation | PP Copolymer | Ferro PP |
| Karina STRAW PVC COMPOUND 550-38/35-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |