Toppyl SP 2001 B is a fully formulated seal peel solution especially developed for the blown ?lm technology. This product has been designed to offer a peelable seal to PE substrates or to seal & peel against itself and is suitable for non-sterilisable applications. Toppyl SP 2001 B is a solution created to replace completely the sealing layer in a coextruded ?lm. It provides a constant easy-opening force over a wide sealing temperature window and is readily processable on conventional equipment in both mono and co-extruded structures. EU and FDA compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD | 200 | MPa | ASTM D882 |
| Tensile Strength - MD | ASTM D882 | ||
| Yield | 12.0 | MPa | ASTM D882 |
| Fracture | 28.0 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break) | 580 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A50 |
| Melting Temperature | 113 | °C | DSC |
| Additional Information |
|---|
| Recommended processing temperatures: 170°C to 230°C. In cases were higher temperatures are required please contact your appropriate technical contact for support. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8260-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AMTOPP VS19 | Inteplast Group | PP, Unspecified | AMTOPP |
| Karina STRAW CPVC COMPOUND 790-38/23-CRPC (**) | Karina Ind. e Com. de Plásticos Ltda | CPVC | Karina |
| Plexiglas® Resist zk4BR | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Tribocomp® PA612 CF30 TS12 | Solvay Specialty Polymers | Nylon 612 | Tribocomp® |