SLOVALEN® PQ 91 N
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TBMnUB_SLOVALEN-PQ-91-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Homopolymer PP modified with natural caoutchouc. The addition of thermoplastic caoutchouc causes increased toughness, possible alternative to PP copolymers. General application in all industry branches - packing material, garden flower-pots, toys, furniture industry, fasteners, clamps, hinge, ofice chairs, hangers etc. Delivered in natural mode and in the full RAL colour scale. Shows higher toughness and ITT in comparison with PQ 51N. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 2.0 | % | |
| Flow | 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 300 | % | ISO 527-2 |
| Flexural Modulus | 700 | MPa | ISO 178 |
| Flexural Stress | 20.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 75 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 55.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 115 | °C | ISO 306/B |
| Melting Temperature (DSC) | 140 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Pressure | 60.0 to 70.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® RGF 50 NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| UMG WOOD® W300E | UMG ABS, Ltd. | ABS | UMG WOOD® |
| Geolast™ 703-45 | ExxonMobil Chemical | TPV | Geolast™ |
| Hanwha Total PP RJ500 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| POCAN® KU 2-7241 000000 | LANXESS GmbH | PBT | POCAN® |