DIOSHY® TPU E998M
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | DIOSHY Co.,Ltd. |
| Trademark: | DIOSHY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TB9fTA_DIOSHY-TPU-E998M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIOSHY® TPU E998M is a Thermoplastic Polyurethane Elastomer (Polyether) (TPU-Polyether) material. It is available in Asia Pacific. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | JIS K7311 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | JIS K7311 | ||
| Shore A | 98 | ||
| Shore D | 53 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | 60.0 | mg | JIS K7311 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 16.7 | MPa | JIS K7311 |
| Tensile Strength | 45.1 | MPa | JIS K7311 |
| Tensile Elongation (Break) | 550 | % | JIS K7311 |
| Compression Set (70°C, 22 hr) | 35 | % | JIS K6301 |
| Rebound Resilience (70°C) | 38 | % | JIS K7311 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 16.7 | MPa | JIS K7311 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -39.0 | °C | DSC |
| Vicat Softening Temperature | 125 | °C | JIS K7206 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 GB30 | NUREL, S.A. | Nylon 6 | Promyde® |
| RTV-2 P-20B | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Scolefin 52 T 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| Karina CLEAR PVC COMPOUND BTR-72/201-D-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OTECH PVC OW635A-Molding | OTECH Corporation | PVC, Unspecified | OTECH PVC |