Chemlon® 104 HU
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TB9XBt_Chemlon-104-HU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 104 HU is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 104 HU are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 to 1.7 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 64.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.5 | % | |
| Break | 20 | % | |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 74.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 110 | J/m | |
| 23°C | 170 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 202 | °C | |
| 1.8 MPa, Unannealed | 76.7 | °C | |
| Melting Temperature | 257 | °C | |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 17 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 22 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 254 | °C | |
| Middle Temperature | 257 to 274 | °C | |
| Front Temperature | 263 to 282 | °C | |
| Nozzle Temperature | 263 to 279 | °C | |
| Processing (Melt) Temp | 263 to 279 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 9007 | Formosa Plastics Corporation | HDPE | TAISOX |
| ADDILENE PMD 50203 | ADDIPLAST | PP, Unspecified | ADDILENE |
| Edgetek™ PK-000/000 Natural | PolyOne Corporation | PEEK | Edgetek™ |
| IDI SMC S31 (Glass Content 26%) | IDI Composites International | TS, Unspecified | IDI SMC |
| ULTEM™ 1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |