NORYL GTX™ GTX951W resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TAYbg8_NORYL-GTX-GTX951W-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A new high flow GTX designed for under-the-hood applications such as power distribution boxes, relay boxes and junction boxes. Developmental name: EXNX0151. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 280°C/2.16 kg | 26 | g/10 min | |
| 280°C/5.0 kg | 67 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 66 | % | ASTM D638 |
| Flexural Strength 3(Break, 100 mm Span) | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 93 | J/m | |
| 23°C | 240 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 195 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.60 mm, in Oil) | 22 | kV/mm | ASTM D149 |
| Dissipation Factor (1 MHz) | 0.017 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP501-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| VINIKA® D2151A | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| Zytel® 103HSL BKB080 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Evoprene™ G 614 | AlphaGary | SEBS | Evoprene™ G |
| Greenflex® HN 70 | Versalis S.p.A. | EVA | Greenflex® |