Category: | PP Random Copolymer , Polypropylene Random Copolymer |
Manufacturer: | Lotte Chemical Corporation |
Trademark: | RANPELEN |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | TAVmy2_RANPELEN-J-550K.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
J-550K is a nucleated random copolymer for injection molding applications. This grade is designed to be processed in conventional injection molding equipment and offers super excellent transparency, good stiffness/impact strength balance, high gloss, high hinge property and low smell. |
General Information | |
---|---|
Additive |
|
Features |
|
Uses |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield) | 32.4 | MPa | ASTM D638 |
Tensile Elongation (Break) | > 100 | % | ASTM D638 |
Flexural Modulus | 1270 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact | ASTM D256 | ||
-10°C | 29 | J/m | |
23°C | 54 | J/m |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
Optical | Nominal Value | Unit | Test Method |
---|---|---|---|
Haze | 17 | % | ASTM D1003 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 140 HB | RTP Company | PP, Unspecified | RTP |
VYTEEN PC/ABS 3016 | Lavergne Group | PC+ABS | VYTEEN |
Beamset 1402 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
Carbo-Rite™ B-980 | Lubrizol Advanced Materials, Inc. | PC | Carbo-Rite™ |
Karina BLACK PVC COMPOUND 750-48/1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |