KOPLA PA6 KNG1030F
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T8MNww_KOPLA-PA6-KNG1030F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA6 KNG1030F is a Polyamide 6 (Nylon 6) material filled with glass fiber. It is available in Asia Pacific. Important attributes of KOPLA PA6 KNG1030F are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 152 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8920 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 200 | °C | |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS AX90 | Techno Polymer America, Inc. | ABS | TECHNO ABS |
| Sylvin 2900-95 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| ACCUTECH™ HP0336W40L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Europrene Latice® 5583 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| ELASTOSIL® R 750/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R |