TEKANATE™ G7038
| Category: | PC , Polycarbonate |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKANATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T857r3_TEKANATE-G7038.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TEKANATE™ G7038 is a Polycarbonate (PC) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 38 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 61.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 140 | % | ASTM D638 |
| Flexural Modulus | 2090 | MPa | ASTM D790 |
| Flexural Strength | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 840 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | > 130 | °C | |
| 1.8 MPa, Unannealed | > 130 | °C | |
| Peak Melting Temperature | 270 to 300 | °C | ASTM D2133 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 110 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 54209ZA85 | SO.F.TER. SPA | SBS | Sofprene T® |
| Xuchuan 3070/B-8280 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Etinox® EI-6530 | Ercros, S.A. | PVC, Flexible | Etinox® |
| Elvacite® 2045 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| OP - Acetal H-Acetal 10MF | Oxford Polymers | Acetal (POM) Homopolymer | OP - Acetal |