DOWLEX™ 2108G Linear Low Density Polyethylene Resin is suitable for the production of cast films with high stiffness, good tear strength and outstanding toughness. It can be used in skin layers of coextruded cast films made from DOWLEX resins to provide a surface with good slip properties. Complies with:
Slip Additive: No Antiblock Additive: No |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.6 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 13.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 13.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 43.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 28.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 700 | % | ASTM D882 |
| TD : Break, 25 µm | 830 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | > 60 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 35 | g | ASTM D1922 |
| TD : 25 µm | 640 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 118 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 89 | ASTM D2457 | |
| Haze (25.0 µm) | 3.1 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 熔体温度：220 - 280°C 冷却辊（主/次）温度 20 - 60°C 生产线速度：150 - 300 米/分 建议的厚度范围：10 - 60 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B5309 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Tenac™ 7010 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| DENKA POVAL PC-1000 | Denka Company Limited | PVOH | DENKA POVAL |
| GAPEX® RPP20EU50AL | Ferro Corporation | PP, Unspecified | GAPEX® |
| TECHNYL® B 218 V20 BLACK 21N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |