ULTEM™ 1100F resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T7t7mZ_ULTEM-1100F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA and EU Food Contact compliant. UL94 V0, V2 and 5VA listing. Effective June 2007, this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1100. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 8.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3720 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 70 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3720 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 1500 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 21.7 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 199 | °C | ASTM D648 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI Str | 170 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | ||
| 0.750 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8502 | Colorite Polymers | PVC, Unspecified | Unichem |
| Calprene® 405 | Dynasol Elastomers | SBS | Calprene® |
| APEX® 79-B427D-25 | Teknor Apex Company | PVC, Flexible | APEX® |
| GLS PP YN06 HF | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| POFEX 8200EP80V | POLYROCKS CHEMICAL CO., LTD | TPE | POFEX |