Braskem PE HS5407V1
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T7GRGp_Braskem-PE-HS5407V1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HS5407V1 is a high molecular weight, high-density polyethylene, copolymer. Exhibit an elevated parison swelling, excellent wall thickness uniformity, an improved balance between stiffness and impact, good environmental stress cracking resistance (ESCR) and extended weathering resistance. Application: Blow Molded Large Parts: Intermediate Bulk Container (IBC). Process: Blow Molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 7.0 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.30 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1 | ASTM D1693 | ||
| 2.00mm, 10% Igepal, molded, F50 | 95.0 | hr | ASTM D1693 |
| 2.00mm, 100% Igepal, molded, F50 | > 800 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 35.0 | MPa | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (-40°C) | 375 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 70.0 | °C | ASTM D648 |
| Injection instructions |
|---|
| Recommended Blow Molding Conditions: Feeding Zone: 180°C to 190°C Barrel: 190°to 200°C Die: 210°C Mold Temperature Range: 5°C to 25°C |
| Note Message | |
|---|---|
| 1 . | 0.3mm notched-plaques |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP5120 Black | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Razalen® P121 TR20 | Razin™ Engineering Plastics | PP Impact Copolymer | Razalen® |
| Vytaflex® 20 | Smooth-On, Inc | PUR, Unspecified | Vytaflex® |
| INLUBE INX-TPU-05141 | Infinity LTL Engineered Compounds | TPU, Unspecified | INLUBE |
| Latishield 66-08A G/25-V0KB1 | LATI S.p.A. | Nylon 66 | Latishield |