KRYSTALFLEX™ PE192
| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | KRYSTALFLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T6zAxv_KRYSTALFLEX-PE192.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KRYSTALFLEX PE192 is a high performance aliphatic polyether film intended for processing by lamination into a range of glass/plastics components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 76 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain | 6.21 | MPa | ASTM D412 |
| 300% strain | 12.4 | MPa | ASTM D412 |
| Tensile Strength 2(Yield) | 27.6 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 550 | % | ASTM D412 |
| Tear Strength | 78.8 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -37.8 | °C | DSC |
| Additional Information |
|---|
| Softening Range, TMA: 185 to 250°FTypical Laminating Parameters:Ultimate Temperature: 239 to 284°FUltimate Pressure: 116 to 174 psiSoaking Time: 30 min/0.25 in |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1377A | Teknor Apex Company | TPE | Telcar® |
| VESTAMID® L L-R2-GF25 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Amilan® CM1011G-30 | Toray Resin Company | Nylon 6 | Amilan® |
| Forprene® 6NM901A90 | SO.F.TER. SPA | TPV | Forprene® |
| LOXIM 400 00 HB | LOXIM Industries Private Limited | Nylon 66 | LOXIM |