Retpol® 1094 UVH
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T6ySWf_Retpol-1094-UVH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Corton 1094 UVH is a 20% talc filled copolymer polypropylene compound. It is a medium to high flow injection moulding grade developed for rigid components requiring good impact strength and dimensional stability. It is stabilized to meet continuous outdoor weathering requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.1 to 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 80 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 73 | ||
| Shore D, 15 sec, 3.00 mm | 64 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 48 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 2050 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 41 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 117 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 59.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9658-40 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Laser+® W PJ002 (F43A) | DAK Americas LLC | PET | Laser+® |
| LEXAN™ PC0700 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina CLEAR PVC COMPOUND 80/213-D-IS-SI (DAY BRASIL) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Fortron® 1132L4 | Celanese Corporation | PPS | Fortron® |