LNP™ THERMOCOMP™ RF006SXZ compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T4Y9ho_LNP-THERMOCOMP-RF006SXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF006SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1006 HS Product reorder name: RF006SXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.90 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.67 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.99 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11400 | MPa | ASTM D638 |
| -- | 10700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 200 | MPa | ASTM D638 |
| Yield | 195 | MPa | ISO 527-2/5 |
| Break 3 | 200 | MPa | ASTM D638 |
| Break | 194 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.3 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2/5 |
| Break 5 | 3.3 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9510 | MPa | ASTM D790 |
| -- 7 | 9260 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 279 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 286 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 286 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 10 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 11 | 82 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.5 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 251 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 243 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AMVO TL | Arkema | Nylon 12 | Rilsan® |
| MonoSol® D-7031 XR | MonoSol, LLC | PVOH | MonoSol® |
| TOTAL Polystyrene Impact 4440 (EU) | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Anjatech® 250-E/GF15 | Almaak International GmbH | Nylon 6 | Anjatech® |
| Generic Silicone - Unspecified | Generic | Silicone | Generic |