POCAN® KU 2-7003 POS042 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T29I8h_POCAN-KU-2-7003-POS042-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, non-reinforced, injection molding |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 1.30 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 60.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 2.00 mm 1 | 1.7 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.30 | % | |
| Flow : 260°C, 2.00 mm 3 | 1.7 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2720 | MPa | ASTM D638 |
| 23°C | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield, 23°C | 55.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 48.3 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 8.0 | % | ISO 527-2/50 |
| Break, 23°C | 38 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 23°C | 2380 | MPa | ASTM D790 |
| 23°C 5 | 2700 | MPa | ISO 178/A |
| Flexural Strength | |||
| 23°C | 89.6 | MPa | ASTM D790 |
| 3.5% Strain, 23°C | 80.0 | MPa | ISO 178/A |
| 23°C 6 | 90.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 6.0 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GHR, 09-030 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 200 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | |
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.2E-4 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.2E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6921 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Milastomer™ 6030BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Elastocon® 8078N | Elastocon TPE Technologies | TPE | Elastocon® |
| Hax™ HFC 0108/4 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Kumho PPG 5021 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |