Xmod WD300UBB is a Glass Fibre/Mineral filled polypropylene compound intended for injection moulding. The product is 30% Glass Fibre/Mineral filled. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 67.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 5000 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 0°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 158 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 138 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 111 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability (1.00 mm) | > 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 - 80 °CMass Temperature: 230 - 280 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® B T BK | Ravago Group | Nylon 6 | Ravamid® |
| Toler PP PP2024 | Toler Chemical, Inc | PP Impact Copolymer | Toler PP |
| Axiall PVC SP-7107 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| POCAN® B 3216 HR 000000 | LANXESS GmbH | PBT | POCAN® |
| Moplen RP210G | LyondellBasell Industries | PP Random Copolymer | Moplen |