Ultramid® Seal-Fit
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T1UV8a_Ultramid-Seal-Fit.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, tough, amorphous copolyamide for injection moulding, specially developed for tight overmoulding of metal inlays. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | |||
| 230°C/10.0 kg | 75.0 | -- | cm³/10min | ISO 1133 |
| 275°C/5.0 kg | 120 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.30 | -- | % | ISO 294-4 |
| Flow direction | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 4.5 - 5.0 | -- | % | ISO 62 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 125 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | 65 | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2500 | -- | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | -- | % | ISO 527-2/50 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 57.0 | -- | °C | ISO 75-2/B |
| Vicat Softening Temperature | 68.0 | -- | °C | ISO 306/B |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 8.0E-5 - 1.2E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 - 1.2E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | -- | ohms | IEC 60093 |
| Volume Resistivity | 9.0E+14 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | V-2 | -- | UL 94 |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA6/66/136 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec | ||
| Drying Temperature | 60.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 30.0 | °C | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 240 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® E3000FR | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Sinpolene MBB1406 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| T-Blend® 6100B-SB | TSRC Corporation | TPE | T-Blend® |
| Viton® B-601C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| SQUARE® SSR1501-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |