CERTENE™ LDF-222C
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T143TY_CERTENE-LDF-222C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-222C is a certified prime resin specially designed for production of high clarity Blown films for packaging of articles requiring good opticals such as baked products, sandwich bags, light duty produce bags, toilet paper and textiles. LDF-222C features easy processability, and optimal balance of film strength, stiffness, good openability and excellent sealability. Maximum recommended film drawdown is 1.0 mil. LDF-222C contains medium slip and medium antiblock. LDF-222C complies with FDA regulation 21CFR 177.1520 (c) 2.2 and most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm | 234 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm | 248 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm | 11.0 | MPa | ASTM D882 |
| MD : Broken, 32 µm | 26.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm | 15.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm | 180 | % | ASTM D882 |
| TD : Broken, 32 µm | 550 | % | ASTM D882 |
| Dart Drop Impact 1(32 µm) | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 370 | g | ASTM D1922 |
| TD : 32 µm | 160 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 111 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 75 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 5.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.25 mils (31 µm) film, melt temperature 350-370°F (175-185°C), blow-up-ratio 2.5:1. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ MX5210-0040 RS Natural | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| RTP 383 TFE 10 EM | RTP Company | PC | RTP |
| Quadrant EPP TIVAR® 88-2 ESD | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| SCHULAMID® 66 CF 20 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sylvin 2900-90 Clear 8391 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |