DOW™ HDPE DMDA-8910 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T0XWyT_DOW-HDPE-DMDA-8910-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ DMDA-8910 NT 7 High Density Polyethylene (HDPE) Resin is produced by the UNIPOL™ Process Technology from Dow and is intended for use in injection molded rigid packaging applications including material handling and industrial container applications. The resin is designed to meet rigorous performance characteristics, including environmental stress crack resistance and impact strength, while maintaining excellent processing characteristics beneficial for molders. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.945 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 12.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 24.1 | MPa | ASTM D638 |
| Fracture | 15.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | 260 | % | ASTM D638 |
| Flexural Modulus | ASTM D790B | ||
| 1% secant | 1000 | MPa | ASTM D790B |
| 2% secant | 855 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 124 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed) | 65.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 128 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 116 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行模塑和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-80A-B30 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Nycast 612VS C-90 | Cast Nylons Ltd. | Nylon 612 | Nycast |
| Fiberfil® M-2494 BK | Fiberfil® Engineered Plastics Inc. | Nylon, Unspecified | Fiberfil® |
| Huafon JF-W-3240 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| PHOENIX™ 6851 | Phon Tech Industrial Company | TPE | PHOENIX™ |