LNP™ THERMOCOMP™ UFW49S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T0DAYZ_LNPTHERMOCOMPUFW49Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UFW49S is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized, Low Warpage. Also known as: LNP* THERMOCOMP* Compound UFM-3249 HS Product reorder name: UFW49S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.87 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.25 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 192 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2 |
| Flexural Modulus | 19300 | MPa | ISO 178 |
| Flexural Stress | 274 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(23°C) | 6.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 38 | kJ/m² | ISO 180/1U |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 - 321 | °C | |
| Middle Temperature | 316 - 327 | °C | |
| Front Temperature | 327 - 338 | °C | |
| Processing (Melt) Temp | 316 - 332 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 2103-20 CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Clariant PBT PBT-1300 | Clariant Corporation | PBT | Clariant PBT |
| Lucel® GC210 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |
| Petlon Prime B1-G25-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| Sylvin 8280-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |