Sinkral® PD D 232/M4
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Sinkral® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SyPpai_Sinkral-PD-D-232-M4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Special very low gloss extrusion / co-extrusion grade, with good flow. Designation: Thermoplastic ISO 2580-ABS 1,EGN,105-08-09-15 Sinkral PD D 232/M4 is widely used in the extrusion / co-extrusion of foils, when a very high matt appearance is required, as well as in the extrusion of profiles. This grade is available in natural color only |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus 3 | 1550 | MPa | ASTM D790 |
| Flexural Strength 4 | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | DIN 53453 |
| Charpy Unnotched Impact Strength | DIN 53453 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -40°C, 3.20 mm | 75 | J/m | ISO 180/4A |
| -20°C, 3.20 mm | 80 | J/m | ISO 180/4A |
| 0°C, 3.20 mm | 90 | J/m | ISO 180/4A |
| 23°C, 3.20 mm | 110 | J/m | ISO 180/4A |
| -40°C 5 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 6 | 9.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 101 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ISO 306/A120 |
| -- | 101 | °C | ISO 306/B120 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 kHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 kHz) | 0.015 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastic ISO 2580-ABS 1,EGN,105-08-09-15 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 4 mm |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PC 26 T 20 | SILON s.ro | PP Copolymer | TABOREN |
| Fainplast PVC KL 93/3 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Enviramid® N1350HL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| ESTADIENE 1218 HT V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Sylvin 5170-85 Red 6290 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |