Kepex® 3315GVS
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sy56wI_Kepex-3315GVS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KEPEX 3315GVS is a flame resistant and 15% glass fiber reinforced PBT. It exhibits non-blooming type flame resistance, UL84 V-0 rating, and good mechanical and thermal properties. It is applicable to automotive, electrical, electronic and industrial parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.70 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 96.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5390 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 218 | °C | |
| 1.8 MPa, Unannealed | 200 | °C | |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 230 to 250 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5420 A1 | Spartech Polycom | PP, Unspecified | Spartech |
| NORYL™ NCF1010 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| CYCOLOY™ CY5100 resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| HOPELEN L-670M | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| LNP™ THERMOCOMP™ DX13354 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |