INEOS HDPE T50-4400-119
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sx6Zqg_INEOS-HDPE-T50-4400-119.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| T50-4400-119 is a high-flow, high density polyethylene copolymer intended for high speed injection molding of thin wall containers. This material will allow for cycle time reduction while still imparting reasonable impact strength. This resin meets the Food and Drug Administration requirements of 21CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 44 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, F50) | 1.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 26.2 | MPa | |
| Break | 26.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.8 | % | |
| Break | 7.7 | % | |
| Flexural Modulus - Tangent | 1200 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Notched Izod Impact (Area) (23°C) | 2.60 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 66.1 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN V-235N | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| POLYLAN T-065 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| SUSTAMID 6G MO | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| TAROPRENE® 1 A95 E6N V0 | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Borealis PE CG8410 | Borealis AG | HDPE | Borealis PE |