Kingfa PC-S609
| Category: | PC Alloy , Polycarbonate Alloy |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SwKfQN_Kingfa-PC-S609.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PC-S609 is a polycarbonate alloy (PC alloy) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PC-S609 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 58.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 3 | 2300 | MPa | ASTM D790 |
| Flexural Strength 4 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 450 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 131 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 125 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 |
| Additional Information |
|---|
| Melt Flow Rate, ASTM D1238, 300°C, 1.2Kg: 12 to 16g/10minWeather Resistance, ASTM D4459, 200hr xenon lamp: <1.8 delta E |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 115 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 275°CInjection Speed: 60 to 90% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 127 Z | RTP Company | PP Homopolymer | RTP |
| NITRIFLEX N-7920 | NITRIFLEX | PVC+NBR | NITRIFLEX |
| Dryflex® 500900S | ELASTO | SEBS | Dryflex® |
| ESPOLEX 4855 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| LUVOCOM® 20-8943 | Lehmann & Voss & Co. | PPA | LUVOCOM® |