TOPAS® 9506F-500

Category:	COC , Cyclic Olefin Copolymer
Manufacturer:	Polyplastics Co., Ltd.
Trademark:	TOPAS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	SvoZlx_TOPAS9506F500.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Description
TOPAS 9506F-500 is a low glass transition film extrusion blending grade. It is a medium clarity resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer blended cast applications, and in coextrusions in both cast and blown processes, for a variety of film and sheet products. Leading applications include shrink film and labels where shrinkage at moderate temperatures is desired. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.

Selected Applications

Shrink films and labels

Thermoformed PE films

Food packaging

Healthcare and food contact

Leading Attributes

High shrink, low stress, gloss, clarity, toughness

Improved material distribution, stiffness, depth

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Packaging and Film Extrusion

TOPAS 9506F-04 - high clarity extrusion grade

General Information
Features	High purity Moisture proof Rigidity, high Highlight Copolymer Good chemical resistance Good toughness Compliance of Food Exposure High shrinkage BPA-free Halogen-free Medium transparency
Uses	Films Label Mixing cast film Sheet Food packaging Medical/nursing supplies
Agency Ratings	FDA FCN 405 Europe 10/1/2011 12:00:00 AM
Forms	Particle
Processing Method	Film extrusion Blow film Co-extruded film cast film Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.02	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	0.90	g/10 min	ISO 1133
230°C/2.16 kg	5.5	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR)			ISO 1133
190°C/2.16 kg	1.00	cm³/10min	ISO 1133
230°C/2.16 kg	6.00	cm³/10min	ISO 1133
Water Absorption (Saturation, 23°C)	0.010	%	ISO 62

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	70	µm
Tensile Modulus			ISO 527-3/1
MD : 70 µm, cast film	1700	MPa	ISO 527-3/1
TD : 70 µm, cast film	2000	MPa	ISO 527-3/1
Tensile Stress			ISO 527-3/50
MD : Fracture, 70 µm, cast film	55.0	MPa	ISO 527-3/50
TD : Fracture, 70 µm, cast film	55.0	MPa	ISO 527-3/50
Tensile Elongation			ISO 527-3/50
MD : Fracture, 70 µm, cast film	2.9	%	ISO 527-3/50
TD : Fracture, 70 µm, cast film	3.6	%	ISO 527-3/50
Dart Drop Impact (70 µm, cast film)	< 36	g	ISO 7765-1
Elmendorf Tear Strength			ISO 6383-2
MD : 70 µm, cast film	2.3	N	ISO 6383-2
TD : 70 µm, cast film	2.4	N	ISO 6383-2
Water Vapor Transmission Rate (70 µm, 23°C, Cast Film, 85% RH)	0.11	g·mm/m²/atm/24 hr	ASTM F1249

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	65.0	°C	ISO 11357-2

Optical	Nominal Value	Unit	Test Method
Gloss (60, 70.0 µm, cast film)	> 100		ISO 2813
Haze (70.0 µm, cast film)	> 2.0	%	ISO 14782

Extrusion	Nominal Value	Unit
Feed part of extruder	20 - 60	°C
Extruder Screw L/D Ratio	> 28:1
Cylinder Zone 1 Temp.	200 - 210	°C
Cylinder Zone 2 Temp.	200 - 210	°C
Cylinder Zone 3 Temp.	200 - 210	°C
Cylinder Zone 4 Temp.	200 - 210	°C
Die Temperature	220 - 230	°C

Extrusion instructions
Head pressure: P > 140 bar / 2000 psi; Fine screen packs as neededScrew speed: RPM > 50% nominalScrew design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 inch Grooved Feed: Hot temperature: 120°C (248°F)

Resin Grade	Manufacturer	Category	Trademark
Tecnoflon® P 959	Solvay Specialty Polymers	Fluorelastomer	Tecnoflon®
XANTAR® F 25 UR	Mitsubishi Engineering-Plastics Corp	PC	XANTAR®
ADDINYL B2 V20	ADDIPLAST	Nylon 6	ADDINYL
KEP® 2371	Kumho Polychem Co., Ltd.	EPDM	KEP®
Sylvin 3210-75 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin