| Celanex 1642Z is a general purpose, 20% fiberglass reinforced PBT with a good balance of mechanical properties and processability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| shrinkage- Flow | 0.40 - 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6250 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 96.5 | MPa | ASTM D638 |
| Fracture | 105 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 4.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.3 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 7.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20 - 50 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65 - 93 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S RV250 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Baoding 76E80 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Diamond GPPS GP-550P | Diamond Polystyrene | PS (GPPS) | Diamond GPPS |
| LAPEROS® HA475 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| Karina IVORY PVC COMPOUND 951-35/4-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |