Next Nylon 6 Prime Series NM15-01BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sv1sCg_Next-Nylon-6-Prime-Series-NM15-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Mineral Reinforced Filled Black Compound Product Applications Automotive Industries, power train/Engine Such as Engine hood, wheel cover, Lamp housing etc Benefits Good Dimensional stability and low warpage |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.25 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.52 | -- | % | |
| Across Flow | 0.68 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.8 | -- | % | |
| Saturation 1 | 6.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 105 | -- | ||
| R-Scale | 115 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 70.0 | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | 15 | % | ASTM D638 |
| Flexural Modulus | 2900 | -- | MPa | ASTM D790 |
| Flexural Strength | 90.0 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | 88 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 195 | -- | °C | |
| 1.8 MPa, Unannealed | 130 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Mold Temperature | 85.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 118N | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| TAIRIREX GP550N | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| Monprene® MP-3955B | Teknor Apex Company | TPE | Monprene® |
| NILENE® P K20T | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| ACRYLITE® Satinice df23 8N | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |