Sindustris PP TE5105
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Suyqf0_Sindustris-PP-TE5105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PP TE5105 is a polypropylene material and contains mineral fillers. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of Sindustris PP TE5105 are:
The typical application field of Sindustris PP TE5105 is: automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.90 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 17.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 200 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1270 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 24.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C, 6.40 mm | 62 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 460 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 115 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 1320 | Huntsman Corporation | PAO | REXtac® APAO |
| Niretan B F10 | Soredi S.p.a. | Nylon 6 | Niretan B |
| Optix® CP-1000I | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |
| PolyBlend™ 1100 60A | CardioTech International, Inc. | PUR, Unspecified | PolyBlend™ |
| Dryflex® SE 40A001 | ELASTO | TPE | Dryflex® |