Order Products : sales@su-jiao.com
Adflex KS021P
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Suu1GC_Adflex-KS021P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex KS021P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is suitable for the extrusion and calendering of soft film and sheet, for the impact modification of polypropylene, as well as monolayer and multilayer air quenched blown films. It is also used by our customers as high cold impact resistance material for automotive color-matched interior trim applications. Key characteristics are flexibility and low temperature impact resistance. The grade is available in natural pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 38 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 8.00 | MPa | |
| Break, 23°C | 13.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 38 | % | |
| Break, 23°C | > 800 | % | |
| Flexural Modulus - Chord 1(23°C) | 300 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 85.0 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C, Partial Break | 86 | kJ/m² | |
| 23°C, Partial Break | 52 | kJ/m² | |
| Instrumented Dart Impact 3 | ASTM D3763 | ||
| -40°C, 3.20 mm, Energy at Peak Load, Brittle Failure | 23.0 | J | |
| 23°C, 3.20 mm, Energy at Peak Load, Ductile Failure | 17.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 48.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 38.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/A50 |
| Melting Temperature | 161 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Die C, 50 mm/min |
| 3 . | 6.60 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA U500 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| AGILITY™ 6047 | The Dow Chemical Company | HDPE | AGILITY™ |
| Badamid® C70 | Bada AG | Nylon 66/6 | Badamid® |
| Ferro PP TPP40AE53HB BLACK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Lucofin® 1492M HG | Lucobit AG | EBA | Lucofin® |