VENYL UN002 - 5321
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SuGz1q_VENYL-UN002---5321.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UN002 - 5321 is a polyamide 66 lubrificated and coloured with medium viscosity intended for Injection moulding. APPLICATIONS VENYL UN002 - 5321 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL UN002 - 5321 is available in both black (VENYL UN002 - 8229) and natural (VENYL UN002) but other colours can be provided on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.3 to 2.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 to 2.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 103 | 87 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 to 3500 | 1400 to 1600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 to 95.0 | 60.0 to 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 to 50 | 200 to 300 | % | ISO 527-2 |
| Flexural Modulus | 2600 to 2900 | 1300 to 1500 | MPa | ISO 178 |
| Flexural Stress | 135 to 150 | 75.0 to 85.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.7 to 5.5 | 17 to 23 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 51 to 660 | 180 to 200 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 850 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 270 to 285 | °C | |
| Middle Temperature | 265 to 280 | °C | |
| Front Temperature | 260 to 275 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL6F 801-SB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| TIPPLEN® H 650 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| Vyncolit® E 8436FR-397 | Vyncolit N.V. | Epoxy | Vyncolit® |
| Elastron® G G301.A75.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Bapolene® 270F | Bamberger Polymers, Inc. | LDPE | Bapolene® |