RTP 300 GB 10 TFE 13 SI 2
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Su4wYI_RTP-300-GB-10-TFE-13-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm, Injection Molded | 0.50 | % | |
| 6.35 mm, Injection Molded | 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 2410 | MPa | ASTM D638 |
| Tensile Strength | 41.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 2340 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, Injection Molded | 143 | °C | |
| 1.8 MPa, Unannealed, Injection Molded | 138 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 249 to 293 | °C | |
| Middle Temperature | 249 to 293 | °C | |
| Front Temperature | 249 to 293 | °C | |
| Mold Temperature | 66.0 to 93.0 | °C | |
| Injection Pressure | 69.0 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 3211 | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Vydyne® 21Z | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ACRYLITE® MD™ L40 | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® MD™ |
| BMC 901 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Geon™ Vinyl Flexible 90067 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |