ColorFast® NY1GF330
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Stpcmm_ColorFast-NY1GF330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% glass-filled nylon 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.9 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 138 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.0 | % | |
| Break | 3.0 | % | |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 221 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 30 to 60 | % | |
| Rear Temperature | 260 to 293 | °C | |
| Middle Temperature | 266 to 293 | °C | |
| Front Temperature | 266 to 293 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Processing (Melt) Temp | 279 to 304 | °C | |
| Mold Temperature | 37.8 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 60 to 120 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP5140R B1 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| APICAL 300AF021 | Kaneka Corporation | PI, TS | APICAL |
| GLAMIDE® T-222SA | TOYOBO America, Inc. | Nylon 6 Elast | GLAMIDE® |
| HiFill® POM CO 0167 S2 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| LNP™ LUBRILOY™ Z20001 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRILOY™ |