LG SAN 80HF
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | StELcs_LG-SAN-80HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Transparency, Heat Resistance, Chemical Resistance Application Refrigerator Sleeves, Miscellaneous |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 | g/cm³ | ASTM D792 |
| -- | 1070 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 3.0 | g/10 min | |
| 220°C/10.0 kg | 29 | g/10 min | |
| 230°C/3.8 kg | 10 | g/10 min | |
| Melt volume-flow rate (220°C/10.0 kg) | 31.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.16 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm 4 | 3110 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2 5 |
| Tensile Strength | |||
| Yield, 3.20 mm 6 | 73.5 | MPa | ASTM D638 |
| Break | 70.0 | MPa | ISO 527-2 7 |
| Tensile Elongation | |||
| Break, 3.20 mm 8 | 6.0 | % | ASTM D638 |
| Break | 6.0 | % | ISO 527-2 9 |
| Flexural Modulus 10(3.20 mm) | 3680 | MPa | ASTM D790 |
| Flexural Strength 11(3.20 mm) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 12 | ||
| -30°C | 2.00 | kJ/m² | |
| 23°C | 2.80 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 13 | ||
| -30°C | 4.80 | kJ/m² | |
| 23°C | 13.0 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 9.8 | J/m | |
| 23°C, 6.40 mm | 9.8 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 90.0 | °C | ASTM D648 |
| Glass Transition Temperature 14 | 110 | °C | ISO 11357-2 15 |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ASTM D1525 |
| 50°C/h, B (50N) | 100 | °C | ISO 306 16 |
| CLTE | ISO 11359-2 17 | ||
| Flow | 6.7E-5 | cm/cm/°C | |
| Transverse | 6.7E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 18 |
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 19 |
| Electric strength | 51 | kV/mm | IEC 60243-1 20 |
| Comparative tracking index | 375 | IEC 60112 21 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 22 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 190 to 220 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | 1.0 mm/min |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | 50 mm/min |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | 50 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 15 mm/min |
| 11 . | 15 mm/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | 10 °C/min |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starpylen HU 70E3 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Cereplast Hybrid Resins® 101 | Cereplast, Inc. | PP Alloy | Cereplast Hybrid Resins® |
| Dorlyl PVC GFG 52D | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |
| Geon™ Vinyl Wire & Cable WJKC302R | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| VALOX™ EH7020HF resin | SABIC Innovative Plastics Asia Pacific | PBT+PET | VALOX™ |